N08135 Stainless Steel vs. EN 1.3533 Steel

Both N08135 stainless steel and EN 1.3533 steel are iron alloys. They have 42% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.3533 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 570
690 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
440
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
5.0
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
1.8
Embodied Energy, MJ/kg 94
25
Embodied Water, L/kg 220
60

Common Calculations

PREN (Pitting Resistance) 38
2.1
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
24 to 50
Strength to Weight: Bending, points 19
22 to 36
Thermal Shock Resistance, points 13
20 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.15 to 0.2
Chromium (Cr), % 20.5 to 23.5
1.3 to 1.6
Copper (Cu), % 0 to 0.7
0 to 0.3
Iron (Fe), % 30.2 to 42.3
92.9 to 94.9
Manganese (Mn), % 0 to 1.0
0.4 to 0.7
Molybdenum (Mo), % 4.0 to 5.0
0.15 to 0.25
Nickel (Ni), % 33 to 38
3.3 to 3.8
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0