N08330 Stainless Steel vs. AWS E409Nb

Both N08330 stainless steel and AWS E409Nb are iron alloys. They have 58% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is AWS E409Nb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 550
500
Tensile Strength: Yield (Proof), MPa 230
380

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
25
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 32
13
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
2.9
Embodied Energy, MJ/kg 77
42
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 19
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
380
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 3.1
6.8
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 17 to 20
11 to 14
Copper (Cu), % 0 to 1.0
0 to 0.75
Iron (Fe), % 38.3 to 48.3
80.2 to 88.5
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 34 to 37
0 to 0.6
Niobium (Nb), % 0
0.5 to 1.5
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.75 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0 to 0.025
0