N08330 Stainless Steel vs. AWS E430

Both N08330 stainless steel and AWS E430 are iron alloys. They have 61% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is AWS E430.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 550
500

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1340
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
25
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 32
9.0
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
2.2
Embodied Energy, MJ/kg 77
31
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 19
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 3.1
6.7
Thermal Shock Resistance, points 13
13

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.1
Chromium (Cr), % 17 to 20
15 to 18
Copper (Cu), % 0 to 1.0
0 to 0.75
Iron (Fe), % 38.3 to 48.3
77.8 to 85
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 34 to 37
0 to 0.6
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.75 to 1.5
0 to 0.9
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0 to 0.025
0