Both N08330 stainless steel and EN 1.4938 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is EN 1.4938 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
16 to 17
Fatigue Strength, MPa 190
390 to 520
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 360
540 to 630
Tensile Strength: Ultimate (UTS), MPa 550
870 to 1030
Tensile Strength: Yield (Proof), MPa 230
640 to 870

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 420
390
Maximum Temperature: Mechanical, °C 1050
750
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
30
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 32
10
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
3.3
Embodied Energy, MJ/kg 77
47
Embodied Water, L/kg 190
110

Common Calculations

PREN (Pitting Resistance) 19
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 140
1050 to 1920
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
31 to 37
Strength to Weight: Bending, points 18
26 to 29
Thermal Diffusivity, mm2/s 3.1
8.1
Thermal Shock Resistance, points 13
30 to 35

Alloy Composition

Carbon (C), % 0 to 0.080
0.080 to 0.15
Chromium (Cr), % 17 to 20
11 to 12.5
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 38.3 to 48.3
80.5 to 84.8
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.4 to 0.9
Molybdenum (Mo), % 0
1.5 to 2.0
Nickel (Ni), % 34 to 37
2.0 to 3.0
Nitrogen (N), % 0
0.020 to 0.040
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.75 to 1.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Tin (Sn), % 0 to 0.025
0
Vanadium (V), % 0
0.25 to 0.4