N08330 Stainless Steel vs. EN 1.8838 Steel

Both N08330 stainless steel and EN 1.8838 steel are iron alloys. They have 45% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is EN 1.8838 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
19
Fatigue Strength, MPa 190
290
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 360
380
Tensile Strength: Ultimate (UTS), MPa 550
610
Tensile Strength: Yield (Proof), MPa 230
430

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
410
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
44
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 32
2.6
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.7
Embodied Energy, MJ/kg 77
23
Embodied Water, L/kg 190
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
500
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 3.1
12
Thermal Shock Resistance, points 13
18

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0 to 0.080
0 to 0.18
Chromium (Cr), % 17 to 20
0 to 0.35
Copper (Cu), % 0 to 1.0
0 to 0.6
Iron (Fe), % 38.3 to 48.3
95 to 99.985
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0 to 1.8
Molybdenum (Mo), % 0
0 to 0.23
Nickel (Ni), % 34 to 37
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.75 to 1.5
0 to 0.65
Sulfur (S), % 0 to 0.030
0 to 0.025
Tin (Sn), % 0 to 0.025
0
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.14