S32053 Stainless Steel vs. EN 1.8519 Steel

Both S32053 stainless steel and EN 1.8519 steel are iron alloys. They have 49% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.8519 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
360
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
10
Fatigue Strength, MPa 310
630
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 510
710
Tensile Strength: Ultimate (UTS), MPa 730
1200
Tensile Strength: Yield (Proof), MPa 330
1030

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
450
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 33
3.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.9
Embodied Energy, MJ/kg 83
26
Embodied Water, L/kg 210
58

Common Calculations

PREN (Pitting Resistance) 44
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
120
Resilience: Unit (Modulus of Resilience), kJ/m3 270
2790
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
43
Strength to Weight: Bending, points 22
32
Thermal Diffusivity, mm2/s 3.3
11
Thermal Shock Resistance, points 16
35

Alloy Composition

Carbon (C), % 0 to 0.030
0.27 to 0.34
Chromium (Cr), % 22 to 24
2.3 to 2.7
Iron (Fe), % 41.7 to 48.8
95.7 to 97.1
Manganese (Mn), % 0 to 1.0
0.4 to 0.7
Molybdenum (Mo), % 5.0 to 6.0
0.15 to 0.25
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035
Vanadium (V), % 0
0.1 to 0.2