S32053 Stainless Steel vs. SAE-AISI 1044 Steel

Both S32053 stainless steel and SAE-AISI 1044 steel are iron alloys. They have 46% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is SAE-AISI 1044 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
18
Fatigue Strength, MPa 310
230
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
46
Shear Modulus, GPa 80
72
Shear Strength, MPa 510
380
Tensile Strength: Ultimate (UTS), MPa 730
620
Tensile Strength: Yield (Proof), MPa 330
340

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.8
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.4
Embodied Energy, MJ/kg 83
18
Embodied Water, L/kg 210
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
94
Resilience: Unit (Modulus of Resilience), kJ/m3 270
320
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 16
20

Alloy Composition

Carbon (C), % 0 to 0.030
0.43 to 0.5
Chromium (Cr), % 22 to 24
0
Iron (Fe), % 41.7 to 48.8
98.8 to 99.27
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0 to 0.050