S32654 Stainless Steel vs. ASTM A182 Grade F24

Both S32654 stainless steel and ASTM A182 grade F24 are iron alloys. They have 46% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is ASTM A182 grade F24.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
210
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 45
23
Fatigue Strength, MPa 450
330
Poisson's Ratio 0.28
0.29
Reduction in Area, % 46
45
Shear Modulus, GPa 82
74
Shear Strength, MPa 590
420
Tensile Strength: Ultimate (UTS), MPa 850
670
Tensile Strength: Yield (Proof), MPa 490
460

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1100
460
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 11
39
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 34
4.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.4
2.3
Embodied Energy, MJ/kg 87
33
Embodied Water, L/kg 220
61

Common Calculations

PREN (Pitting Resistance) 57
6.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
140
Resilience: Unit (Modulus of Resilience), kJ/m3 570
570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
24
Strength to Weight: Bending, points 25
22
Thermal Diffusivity, mm2/s 2.9
11
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0015 to 0.0070
Carbon (C), % 0 to 0.020
0.050 to 0.1
Chromium (Cr), % 24 to 25
2.2 to 2.6
Copper (Cu), % 0.3 to 0.6
0
Iron (Fe), % 38.3 to 45.3
94.5 to 96.1
Manganese (Mn), % 2.0 to 4.0
0.3 to 0.7
Molybdenum (Mo), % 7.0 to 8.0
0.9 to 1.1
Nickel (Ni), % 21 to 23
0
Nitrogen (N), % 0.45 to 0.55
0 to 0.12
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.5
0.15 to 0.45
Sulfur (S), % 0 to 0.0050
0 to 0.010
Titanium (Ti), % 0
0.060 to 0.1
Vanadium (V), % 0
0.2 to 0.3