S32654 Stainless Steel vs. AWS E309Nb

Both S32654 stainless steel and AWS E309Nb are iron alloys. They have 81% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is AWS E309Nb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 45
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
78
Tensile Strength: Ultimate (UTS), MPa 850
620

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 11
15
Thermal Expansion, µm/m-K 15
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 34
25
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.4
4.4
Embodied Energy, MJ/kg 87
64
Embodied Water, L/kg 220
180

Common Calculations

PREN (Pitting Resistance) 57
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
22
Strength to Weight: Bending, points 25
21
Thermal Diffusivity, mm2/s 2.9
4.0
Thermal Shock Resistance, points 19
16

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.12
Chromium (Cr), % 24 to 25
22 to 25
Copper (Cu), % 0.3 to 0.6
0 to 0.75
Iron (Fe), % 38.3 to 45.3
54.8 to 64.8
Manganese (Mn), % 2.0 to 4.0
0.5 to 2.5
Molybdenum (Mo), % 7.0 to 8.0
0 to 0.75
Nickel (Ni), % 21 to 23
12 to 14
Niobium (Nb), % 0
0.7 to 1.0
Nitrogen (N), % 0.45 to 0.55
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.030