S32654 Stainless Steel vs. EN 1.3537 Steel

Both S32654 stainless steel and EN 1.3537 steel are iron alloys. They have 45% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.3537 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190 to 220
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 82
73
Tensile Strength: Ultimate (UTS), MPa 850
620 to 730

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
440
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 11
43
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 34
2.8
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.4
1.5
Embodied Energy, MJ/kg 87
21
Embodied Water, L/kg 220
54

Common Calculations

PREN (Pitting Resistance) 57
2.6
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
22 to 26
Strength to Weight: Bending, points 25
21 to 23
Thermal Diffusivity, mm2/s 2.9
12
Thermal Shock Resistance, points 19
18 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.020
0.93 to 1.1
Chromium (Cr), % 24 to 25
1.7 to 2.0
Copper (Cu), % 0.3 to 0.6
0 to 0.3
Iron (Fe), % 38.3 to 45.3
96.4 to 97.8
Manganese (Mn), % 2.0 to 4.0
0.25 to 0.45
Molybdenum (Mo), % 7.0 to 8.0
0.15 to 0.3
Nickel (Ni), % 21 to 23
0
Nitrogen (N), % 0.45 to 0.55
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0.15 to 0.45
Sulfur (S), % 0 to 0.0050
0 to 0.030