S32654 Stainless Steel vs. EN 1.4369 Stainless Steel

Both S32654 stainless steel and EN 1.4369 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.4369 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
260
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 45
40
Fatigue Strength, MPa 450
330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
77
Shear Strength, MPa 590
580
Tensile Strength: Ultimate (UTS), MPa 850
850
Tensile Strength: Yield (Proof), MPa 490
390

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 1100
940
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 11
15
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 34
14
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.4
3.0
Embodied Energy, MJ/kg 87
43
Embodied Water, L/kg 220
150

Common Calculations

PREN (Pitting Resistance) 57
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
280
Resilience: Unit (Modulus of Resilience), kJ/m3 570
380
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
31
Strength to Weight: Bending, points 25
26
Thermal Diffusivity, mm2/s 2.9
4.0
Thermal Shock Resistance, points 19
18

Alloy Composition

Carbon (C), % 0 to 0.020
0.070 to 0.15
Chromium (Cr), % 24 to 25
17.5 to 19.5
Copper (Cu), % 0.3 to 0.6
0
Iron (Fe), % 38.3 to 45.3
63 to 70.2
Manganese (Mn), % 2.0 to 4.0
5.0 to 7.5
Molybdenum (Mo), % 7.0 to 8.0
0
Nickel (Ni), % 21 to 23
6.5 to 8.5
Nitrogen (N), % 0.45 to 0.55
0.2 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0.5 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.015