S32654 Stainless Steel vs. EN 1.4525 Stainless Steel

Both S32654 stainless steel and EN 1.4525 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.4525 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 45
5.6 to 13
Fatigue Strength, MPa 450
480 to 540
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
76
Tensile Strength: Ultimate (UTS), MPa 850
1030 to 1250
Tensile Strength: Yield (Proof), MPa 490
840 to 1120

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 440
430
Maximum Temperature: Mechanical, °C 1100
860
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 11
18
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 34
13
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.4
2.8
Embodied Energy, MJ/kg 87
39
Embodied Water, L/kg 220
130

Common Calculations

PREN (Pitting Resistance) 57
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
68 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 570
1820 to 3230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
36 to 45
Strength to Weight: Bending, points 25
29 to 33
Thermal Diffusivity, mm2/s 2.9
4.7
Thermal Shock Resistance, points 19
34 to 41

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.070
Chromium (Cr), % 24 to 25
15 to 17
Copper (Cu), % 0.3 to 0.6
2.5 to 4.0
Iron (Fe), % 38.3 to 45.3
70.4 to 79
Manganese (Mn), % 2.0 to 4.0
0 to 1.0
Molybdenum (Mo), % 7.0 to 8.0
0 to 0.8
Nickel (Ni), % 21 to 23
3.5 to 5.5
Niobium (Nb), % 0
0 to 0.35
Nitrogen (N), % 0.45 to 0.55
0 to 0.050
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.8
Sulfur (S), % 0 to 0.0050
0 to 0.025