S32654 Stainless Steel vs. EN 1.4530 Stainless Steel

Both S32654 stainless steel and EN 1.4530 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.4530 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
76
Tensile Strength: Ultimate (UTS), MPa 850
1030 to 1370

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 440
450
Maximum Temperature: Mechanical, °C 1100
790
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 15
11

Otherwise Unclassified Properties

Base Metal Price, % relative 34
15
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 6.4
3.4
Embodied Energy, MJ/kg 87
46
Embodied Water, L/kg 220
130

Common Calculations

PREN (Pitting Resistance) 57
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
36 to 48
Strength to Weight: Bending, points 25
29 to 35
Thermal Shock Resistance, points 19
35 to 47

Alloy Composition

Aluminum (Al), % 0
0.6 to 0.8
Carbon (C), % 0 to 0.020
0 to 0.015
Chromium (Cr), % 24 to 25
11.5 to 12.5
Copper (Cu), % 0.3 to 0.6
0
Iron (Fe), % 38.3 to 45.3
74.4 to 77.3
Manganese (Mn), % 2.0 to 4.0
0 to 0.1
Molybdenum (Mo), % 7.0 to 8.0
1.9 to 2.2
Nickel (Ni), % 21 to 23
8.5 to 9.5
Nitrogen (N), % 0.45 to 0.55
0 to 0.010
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.0050
0 to 0.0050
Titanium (Ti), % 0
0.28 to 0.37