S32654 Stainless Steel vs. EN 1.4557 Stainless Steel

Both S32654 stainless steel and EN 1.4557 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.4557 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
160
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 45
40
Fatigue Strength, MPa 450
260
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
80
Tensile Strength: Ultimate (UTS), MPa 850
560
Tensile Strength: Yield (Proof), MPa 490
300

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 1100
1090
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
460
Thermal Conductivity, W/m-K 11
15
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 34
29
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 6.4
5.6
Embodied Energy, MJ/kg 87
76
Embodied Water, L/kg 220
190

Common Calculations

PREN (Pitting Resistance) 57
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
190
Resilience: Unit (Modulus of Resilience), kJ/m3 570
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
19
Strength to Weight: Bending, points 25
19
Thermal Diffusivity, mm2/s 2.9
4.0
Thermal Shock Resistance, points 19
12

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.020
Chromium (Cr), % 24 to 25
19.5 to 20.5
Copper (Cu), % 0.3 to 0.6
0.5 to 1.0
Iron (Fe), % 38.3 to 45.3
49.5 to 56.3
Manganese (Mn), % 2.0 to 4.0
0 to 1.2
Molybdenum (Mo), % 7.0 to 8.0
6.0 to 7.0
Nickel (Ni), % 21 to 23
17.5 to 19.5
Nitrogen (N), % 0.45 to 0.55
0.18 to 0.24
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.010