S32654 Stainless Steel vs. EN 1.4849 Stainless Steel

Both S32654 stainless steel and EN 1.4849 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.4849 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
140
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 45
4.5
Fatigue Strength, MPa 450
120
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
75
Tensile Strength: Ultimate (UTS), MPa 850
480
Tensile Strength: Yield (Proof), MPa 490
250

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 440
620
Maximum Temperature: Mechanical, °C 1100
1020
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1410
1340
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 11
12
Thermal Expansion, µm/m-K 15
15

Otherwise Unclassified Properties

Base Metal Price, % relative 34
42
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 6.4
7.1
Embodied Energy, MJ/kg 87
100
Embodied Water, L/kg 220
200

Common Calculations

PREN (Pitting Resistance) 57
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
18
Resilience: Unit (Modulus of Resilience), kJ/m3 570
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
17
Strength to Weight: Bending, points 25
17
Thermal Diffusivity, mm2/s 2.9
3.2
Thermal Shock Resistance, points 19
11

Alloy Composition

Carbon (C), % 0 to 0.020
0.3 to 0.5
Chromium (Cr), % 24 to 25
18 to 21
Copper (Cu), % 0.3 to 0.6
0
Iron (Fe), % 38.3 to 45.3
32.6 to 43.5
Manganese (Mn), % 2.0 to 4.0
0 to 2.0
Molybdenum (Mo), % 7.0 to 8.0
0 to 0.5
Nickel (Ni), % 21 to 23
36 to 39
Niobium (Nb), % 0
1.2 to 1.8
Nitrogen (N), % 0.45 to 0.55
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
1.0 to 2.5
Sulfur (S), % 0 to 0.0050
0 to 0.030