S32654 Stainless Steel vs. SAE-AISI M3 Class 2 Steel

Both S32654 stainless steel and SAE-AISI M3 class 2 steel are iron alloys. They have 52% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is SAE-AISI M3 class 2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 82
77
Tensile Strength: Ultimate (UTS), MPa 850
770 to 2210

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Melting Completion (Liquidus), °C 1450
1620
Melting Onset (Solidus), °C 1410
1570
Specific Heat Capacity, J/kg-K 460
440
Thermal Conductivity, W/m-K 11
26
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 34
25
Density, g/cm3 8.0
8.3
Embodied Carbon, kg CO2/kg material 6.4
12
Embodied Energy, MJ/kg 87
180
Embodied Water, L/kg 220
110

Common Calculations

PREN (Pitting Resistance) 57
33
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 29
26 to 74
Strength to Weight: Bending, points 25
22 to 45
Thermal Diffusivity, mm2/s 2.9
7.2
Thermal Shock Resistance, points 19
24 to 69

Alloy Composition

Carbon (C), % 0 to 0.020
1.2 to 1.3
Chromium (Cr), % 24 to 25
3.8 to 4.5
Copper (Cu), % 0.3 to 0.6
0 to 0.25
Iron (Fe), % 38.3 to 45.3
75.8 to 82.3
Manganese (Mn), % 2.0 to 4.0
0.15 to 0.4
Molybdenum (Mo), % 7.0 to 8.0
4.8 to 6.5
Nickel (Ni), % 21 to 23
0 to 0.3
Nitrogen (N), % 0.45 to 0.55
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0.2 to 0.45
Sulfur (S), % 0 to 0.0050
0 to 0.030
Tungsten (W), % 0
5.0 to 6.8
Vanadium (V), % 0
2.8 to 3.8