S32654 Stainless Steel vs. N08810 Stainless Steel

Both S32654 stainless steel and N08810 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is N08810 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 45
33
Fatigue Strength, MPa 450
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 82
77
Shear Strength, MPa 590
340
Tensile Strength: Ultimate (UTS), MPa 850
520
Tensile Strength: Yield (Proof), MPa 490
200

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 440
490
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1410
1350
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 11
12
Thermal Expansion, µm/m-K 15
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 34
30
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 6.4
5.3
Embodied Energy, MJ/kg 87
76
Embodied Water, L/kg 220
200

Common Calculations

PREN (Pitting Resistance) 57
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
140
Resilience: Unit (Modulus of Resilience), kJ/m3 570
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
18
Strength to Weight: Bending, points 25
18
Thermal Diffusivity, mm2/s 2.9
3.0
Thermal Shock Resistance, points 19
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.020
0.050 to 0.1
Chromium (Cr), % 24 to 25
19 to 23
Copper (Cu), % 0.3 to 0.6
0 to 0.75
Iron (Fe), % 38.3 to 45.3
39.5 to 50.7
Manganese (Mn), % 2.0 to 4.0
0 to 1.5
Molybdenum (Mo), % 7.0 to 8.0
0
Nickel (Ni), % 21 to 23
30 to 35
Nitrogen (N), % 0.45 to 0.55
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6